The Microwave Activation of Cellulose

Fan, Jiajun (2013) The Microwave Activation of Cellulose. PhD thesis, University of York.

[img]
Preview
Text
The Microwave Activation of Cellulose - Jiajun Fan.pdf
Available under License Creative Commons Attribution-Noncommercial-No Derivative Works 2.0 UK: England & Wales.

Download (20Mb) | Preview

Abstract

The aim of this project was to determine a fundamental understanding of the parameters affecting a microwave pyrolysis and microwave hydrolysis process of microcrystalline cellulose, providing a fundamental insight into the processes of cellulose degradation. A systematic investigation into the microwave pyrolysis of cellulose was performed in which the fundamental parameters of microwave power, microwave duration, sample density, sample pre-heating and maximum pyrolysis temperature were studied. About 65wt.% decomposition of microcrystalline cellulose could be achieved, resulting in the formation of ~44wt.% bio-oil or ~26wt.% gas under their optimum microwave pyrolysis conditions. The maximum temperature/heating rate attained during the microwave pyrolysis processes and moisture content played a critical role in the overall extent of decomposition. The temperature of decomposition under microwave activation was ~120oC lower than that of the thermal decomposition, with initiation of the decomposition process occurring at ~180oC. This coincides with the phase change of cellulose structure. However, the resulting pyrolysis bio-oil largely consisted of levoglucosenone, 1,4:3,6-dianhydro-α-D-glucopyranose, levoglucosan and 1,6-anhydro-β-D-glucofuranose. Due to limitations in use of these products, a hydrolysis process to produce simple fermentable sugars was developed. It proved possible to achieve ~80wt.% decomposition of cellulose with ~30-40wt.% fermentable sugars formed. Further to this, the new microwave specific reaction pathway of cellulose decomposition was determined and the degree of freedom of the cellulose enclosed -CH2OH groups were found to be crucial. This mechanism helped explain the key experimental observations such as: high efficiency of microwave treatment; the dependence of the selectivity yield of glucose on the applied microwave density; the observed high glucose to HMF ratio and the influence of the degree of cellulose crystallinity on the results of the hydrolysis.

Item Type: Thesis (PhD)
Academic Units: The University of York > Chemistry (York)
Identification Number/EthosID: uk.bl.ethos.595210
Depositing User: Dr Jiajun Fan
Date Deposited: 08 Apr 2014 08:33
Last Modified: 08 Sep 2016 13:30
URI: http://etheses.whiterose.ac.uk/id/eprint/5537

You do not need to contact us to get a copy of this thesis. Please use the 'Download' link(s) above to get a copy.
You can contact us about this thesis. If you need to make a general enquiry, please see the Contact us page.

Actions (repository staff only: login required)