Helical Magnetic Structure and Transport Properties in epitaxial B20 Fe(1−x)Co(x)Ge films

Spencer, Charles Steven Bolanos (2018) Helical Magnetic Structure and Transport Properties in epitaxial B20 Fe(1−x)Co(x)Ge films. PhD thesis, University of Leeds.

[img]
Preview
Text
Spencer_CSB_Physics_PhD_2018.pdf - Final eThesis - complete (pdf)
Available under License Creative Commons Attribution-Noncommercial-Share Alike 2.0 UK: England & Wales.

Download (50Mb) | Preview

Abstract

We have grown epitaxial single-phase B20 Fe(1−x)Co(x)Ge films on Si (111) substrates films by molecular beam epitaxy. This method is able to produce the whole range of Fe(1−x)Co(x)Ge which are of high quality due to homogeneous layer growth with low surface roughness of 1-2 nm. The films grown are racemic, showing an equal mix of left-handed and right-handed chiral grains, and are strained due the lattice mismatch between the film and substrate. Magnetic measurements showed the FeGe films grown (~ 70 nm thickness) have a saturation moment, Ms = 0.982(7) μB, and ordering temperature, Tc = 280(2) K, both close to bulk value. Ms and Tc were found to decrease monotonically with increasing x and all films were found to have an easy-plane anisotropy. A helical magnetic structure was observed using polarised neutron reflectometry and we found the helix wavelength to vary with composition. A divergence in the wavelength was found at a critical composition xc = 0.5 where a transition from helimagnet to collinear ferromagnet occurred. The temperature dependent resistivity, ρxx(T), was found to be metallic for all compositions and a broad peak with magnetic origin was found to arise for intermediate compositions 0.2 < x < 0.7. The magnetoresistance in Fe(1−x)Co(x)Ge with 0.1 < x < 1 was found to behave similarly to FeGe, however many differences were observed, such as a positive linear magnetoresistance for Fe(0.4)Co(0.6)Ge and a change in conical magnetoresistance scaling beyond Fe(0.5)Co(0.5)Ge. The Hall resistivity showed an increase as well as a sign change in the ordinary Hall effect coefficient, R0, from 0.0122 μΩ cm/T for FeGe to -0.6808 μΩ cm/T for Fe(0.5)Co(0.5)Ge, at 5 K, indicating a large reduction in the carrier concentration and change of carrier type. The anomalous Hall effect was found to increase dramatically on the introduction of Co, increasing by an order of magnitude from FeGe to Fe(0.9)Co(0.1)Ge at 5 K. We find evidence of potential skyrmion structures through the measurement of the topological Hall effect, with features as large as -0.39 μΩ cm for Fe(0.6)Co(0.4)Ge at 5 K. We conclude Fe(1−x)Co(x)Ge is a potential material for further skyrmion study, but direct observation of these topological structures are required to fully attribute the measured effect and progress further.

Item Type: Thesis (PhD)
Keywords: B20, FeGe, FeCoGe, DMI, Skyrmions, Thin films, Chirality, Helical magnetic structure
Academic Units: The University of Leeds > Faculty of Maths and Physical Sciences (Leeds) > School of Physics and Astronomy (Leeds)
Identification Number/EthosID: uk.bl.ethos.741192
Depositing User: Mr Charles S. B. Spencer
Date Deposited: 14 May 2018 16:04
Last Modified: 25 Jul 2018 09:57
URI: http://etheses.whiterose.ac.uk/id/eprint/20225

You do not need to contact us to get a copy of this thesis. Please use the 'Download' link(s) above to get a copy.
You can contact us about this thesis. If you need to make a general enquiry, please see the Contact us page.

Actions (repository staff only: login required)