Bold, P. E. (1990) Multiaxial fatigue crack growth in rail steel. PhD thesis, University of Sheffield.
Abstract
In the introduction to a recent symposium on rolling contact fatigue, R.A.Smith stated that it was difficult to apply our greatly increased understanding of metal fatigue, to rolling contact fatigue, because of "the apparent lack of alternating tensile stresses to drive the cracks." He went on to say "alternating shear stresses are easily found, but the reproduction of continuous crack growth controlled by shear <Mode II in fracture mechanics terms), has proved to be near impossible." This project has demonstrated that under specific conditions this mode of growth does occur. The project began by studying rolling contact fatigue defects, in particular the 'squat' defect in railway lines, and the stress analyses that have been performed on them. It was concluded that the largest stress cycle experienced by the cracks must be a shear stress. It. series of tests were then performed that loaded a crack in pure shear, or a mixture of tension and shear, looking at the effects of using fully reversed shear loading, and the effects of applying tensile mean stresses to reduce the friction on the crack flanks. However these tests all produced less than one millimetre of mode II growth, before the cracks arrested or branched. The final series of tests however applied a tensile load cycle before each shear load cycle. This time coplanar growth was produced, that is the crack grew in the direction of the maximum shear stress. This type of load cycle is a simplification of the load cycle calculated by Bower and Johnson of Cambridge University, where the tensile load is produced by fluid trapped in the crack. Two crack growth rate formulae were produced that fitted the data, indicating that the growth rate was dependent on both the tensile and the shear parts of the cycle.
Metadata
Keywords: | Material degradation & corrosion & fracture mechanics |
---|---|
Awarding institution: | University of Sheffield |
Academic Units: | The University of Sheffield > Faculty of Engineering (Sheffield) > Mechanical Engineering (Sheffield) |
Identification Number/EthosID: | uk.bl.ethos.333031 |
Depositing User: | EThOS Import Sheffield |
Date Deposited: | 02 Dec 2016 14:42 |
Last Modified: | 02 Dec 2016 14:42 |
You do not need to contact us to get a copy of this thesis. Please use the 'Download' link(s) above to get a copy.
You can contact us about this thesis. If you need to make a general enquiry, please see the Contact us page.