Polysaccharide Derived Mesoporous Carbonaceous Materials for Bulky Dyes and Metals Adsorption from Wastewater (Green Chemical Technology for The Production of Polysaccharide Derived Mesoporous Carbonaceous Materials for Wastewater Treatment)

Abdoul, Hayman Jalal (2015) Polysaccharide Derived Mesoporous Carbonaceous Materials for Bulky Dyes and Metals Adsorption from Wastewater (Green Chemical Technology for The Production of Polysaccharide Derived Mesoporous Carbonaceous Materials for Wastewater Treatment). PhD thesis, University of York.

[img] Text (PhD Thesis_Chemistry_University of York,UK)
25-4-15_Final_PhD Thesis_2_Hayman Abdoul_Chemistry_University of York.pdf
Available under License Creative Commons Attribution-Noncommercial-No Derivative Works 2.0 UK: England & Wales.

Download (14Mb)


The current world crisis in the demand for water is a real problem for all forms of life on our planet. For years, scientists have tried to propose various technologies which might be able to clean and reuse contaminated water. It is crucial to develop a sustainable low cost form of technology. This is especially important for Third World countries, where the ability to get high level technology is difficult and ideally, the form of technology should be cheap, simple and based on the local resources. One of the most available local resources is a polysaccharide such as starch, pectin, cellulose or alginic acid. The major goal of this dissertation is to develop a green form of technology to capture potentially harmful, toxic or valuable compounds from waste water using mesoporous carbonaceous materials based on the local polysaccharide resources. To achieve this target, a novel and improved method of synthesis of mesoporous carbonaceous materials from starch (hereafter referred to as StarbonĀ® ) and alginic acid (hereafter referred to as Algibon) was established at the beginning of the project. Based on this method, a number of mesoporous materials with different textural and surface properties have been generated and characterised by various techniques including nitrogen porosimetry, solid state NMR, DRIFT spectroscopy, electron microscopy, elemental analysis and ash content tests. Some of the major water pollutants in industrial wastes are dyes from textile industry and heavy metals from mining, steel industry, welding, batteries, refinery, fertiliser and other processes. Therefore, the produced materials were systematically tested as dye adsorbers. Bulky azodyes, which represent 75% of the current cotton industry market, were selected as model absorbates. A wide range of Algibons and Starbons materials with different properties (from the completely hydrophilic to completely hydrophobic and with different micro/mesopore volumes and ratios) enabled the optimum material to be found for certain types of adsorption process. It was found that in this type of adsorption, Starbons materials cannot compete with commercially available adsorbents. In contrast, Algibon has demonstrated great potential and significantly outperformed the commercially available adsorbents such as activated carbon (up to 6 times more) for the uptake of a range of bulky dyes. The adsorption data reveals that the BET specific surface area (N2-adsorption) was not the only governing factor and that the dominant mesoporous character of these materials, the accessibility of the pores versus the bulkiness of the dyes and the nature of the surface functionality (hydrophobic versus hydrophilic) also played key roles. The maximum adsorption capacity of Algibon prepared at 800o C (A800) is markedly higher than the one recorded for A450 and outperforms Norit as a commercially available activated carbon (AC) adsorbent. It was found that the higher adsorption capacity of A800 relates to a higher surface area in the mesoporous region. Moreover, it was found that the energy of adsorption is smaller for A800 than for AC. This shows that A800 is not only the preferred adsorbent but will also enable a more effective and easier recovery of the dyes. In addition, the project involved the use of the developed Starbon materials to recover metals. This application is crucial not only for the cleaning of waste waters but also for recovering the valuable and critical metals from solid wastes. Some of these metals are in the EU critical list of elements due to their significant demand in modern economy technologies or are substantial components of industrial waste. These elements are in short supply because of their large demand in growing economy and their scarce abundance in the world. Therefore, a variety of Starbons were screened to test the selectivity of the polysaccharide derived carbonaceous materials towards the high value metals from digested solid wastes consisting of Pulverised fly ash (PFA), Red Mud (RM), Bottom ash (BA), Titano gypsum (TiG), Red Titano gypsum (RTiG) and Phospho Gypsum (PG). Further investigation of metals adsorption based on Algibon was systematically conducted. A800 which demonstrated the most promising results early on and was found to be the most stable material, and was used as the adsorber. A solution containing four high value metal ions (i.e. Co, Cu, Ag and Cd) were selected for the adsorption experiment. Investigation focused on the nature of the metal ions and how they affect the kinetic parameters of adsorption in a detailed experimental analysis of the model system. Different types of adsorption isotherms were applied. The maximum adsorption capacity for each metal was found from the fit isotherm type. Kinetic adsorption was tested and kinetic order model study was carried out.

Item Type: Thesis (PhD)
Academic Units: The University of York > Chemistry (York)
Identification Number/EthosID: uk.bl.ethos.647075
Depositing User: Mr Hayman Jalal Abdoul
Date Deposited: 08 May 2015 11:24
Last Modified: 08 Sep 2016 13:32
URI: http://etheses.whiterose.ac.uk/id/eprint/8800

You do not need to contact us to get a copy of this thesis. Please use the 'Download' link(s) above to get a copy.
You can contact us about this thesis. If you need to make a general enquiry, please see the Contact us page.

Actions (repository staff only: login required)